Cobalt Oxide-Containing Glaze/CaAlg Hydrogel Membrane for Degradation of Orange G via Peroxydisulfate Activation

作者：Bin Zhang, 王明林, Liu Y, Jiabao Cui, Kongyin Zhao · 发表于：Gels · 年份：2026 · DOI：10.3390/gels12070645 · 研究领域：Advanced oxidation water treatment、Membrane Separation Technologies、Phosphorus and nutrient management

The sustained expansion of printing and dyeing operations has led to the discharge of large volumes of organic wastewater containing dyes. The resulting environmental pollution demands urgent solutions, making the development of efficient and eco-friendly methods for the elimination of dyeing wastewater critically important. The combination of alginate hydrogel membranes with advanced oxidation processes (AOPs) for water purification represents an emerging approach in the current field of water treatment. In this study, a calcium alginate membrane was loaded with a glaze containing highly active cobalt oxide to fabricate a glaze-calcium alginate (Glaze-CaAlg) composite membrane. The membrane achieved stable degradation of Orange G dye under optimal conditions, and a series of tests were conducted under varying conditions using pollutant concentrations close to those found in real water bodies. Under optimal conditions (glaze loading = 2.5 mL, PMS = 0.3 mmol/L, cross-flow filtration mode), the membrane achieved a 93.7% degradation efficiency of Orange G (10 ppm) within 45 min, with hydroxyl radicals (·OH, ~79%) identified as the predominant reactive species. The Glaze-CaAlg membrane also exhibited excellent reusability, maintaining a degradation efficiency of over 80% for Orange G across five consecutive cycles. Furthermore, sodium citrate was employed to react with the Glaze-CaAlg membrane, enabling the recovery and secondary application of the glaze. Membranes re-fabricated ...