Synergistic Ultramicropore and Hierarchical Pore Engineering in Heteroatom-Doped Carbon for High-Performance Zinc-Ion Capacitors

作者：Jiale Zhang, Ruifang Zhang, Yangbo Du, Shuaihua Zhang, Runze Gao, Xuanqi Huang, Qi Yang, Debin Kong, Zhichang Xiao · 发表于：Nano-Micro Letters · 年份：2026 · DOI：10.1007/s40820-026-02181-0 · 被引用次数：3 · 研究领域：Supercapacitor Materials and Fabrication、Advancements in Battery Materials、Advanced battery technologies research

Abstract Carbonaceous zinc-ion capacitors (ZICs) offer inherent advantages for energy storage, yet the role of pore structures in enabling high zinc-ion capacitance remains underexplored. Herein, a dual-molten-salt regulation strategy is employed to derive N/O/S-doped porous carbon nanomaterials, achieving a high specific surface area (SSA) of 2523 m 2 g −1 with ultramicropores (< 0.86 nm) contributing 30.6% of the total SSA. Structural analyses reveal that increasing molten FeCl 3 content yields materials with comparable heteroatom contents and defect structures, but a progressive shift from ultramicropores to mesopores. Crucially, the individual contributions of the pore structure are decoupled by both in situ characterizations and theoretical simulations: The ultramicropores facilitate the desolvation of [Zn(H 2 O) 6 ] 2+ (ultramicropore effect), while the hierarchical pores ensure rapid ion transport (hierarchical pore effect). The optimized HHPC-2 delivers a high specific capacitance of 222.6 F g −1 at 1 A g −1 and an energy density of 120.0 Wh kg −1 in ZICs. Intriguingly, its outstanding oxygen reduction reaction catalytic activity enables self-charging upon air exposure after a full discharge, achieving a self-charging rate of 15 mAh g −1 h −1 and recovering 80% of the externally charged capacity in subsequent discharge cycles. This positions the device as highly promising for practical deployment in regions with intermittent grid power supplies.