Comparison of Direct Arylation and Zinc-Mediated Polymerizations for Naphthalenediimide–Bithiazole Polymers with Focus on Efficiency, Structure and Green Metrics

作者：Giacomo Forti, Marc-Antoine Stoeckel, Yongjoon Cho, Matteo Palesati, Mark Weber, L. Ye, S. H. Chung, Robert M. Pankow, Brendan P. Kerwin, Boseok Kang, Simone Fabiano, Natalie Stingelin, A. Facchetti, Tobin J. Marks · 发表于：Chemistry of Materials · 年份：2026 · DOI：10.1021/acs.chemmater.5c02353 · 被引用次数：1 · 研究领域：Conducting polymers and applications、Organic Electronics and Photovoltaics、Synthesis and properties of polymers

The synthesis of n-type semiconductors traditionally relies on the environmentally harmful Stille organotin polymerization. Here, we report the optimized direct arylation polymerization (DARP) of an electron-transporting polymer, poly[2,7-bis(2-decyltetradecyl)-4-methyl-9-(2′-methyl-[5,5′-bithiazol]-2-yl)benzo[lmn]-[3,8]phenanthroline-1,3,6,8(2 H,7 H )-tetraone], P(NDI2DT-Tz2) . A series of PNDITZ-Mn polymers with molecular masses ( M n ) from 6.5 to 32.9 kg mol –1 was synthesized and investigated for charge transport and thermoelectric properties. Optimized DARP conditions yielded PNDITZ-19 K ( M n / D̵ = 18.8 kg mol –1 /2.8), comparable to Zn-PNDITZ prepared via the anionic zinc protocol (16.4 kg mol –1 /2.39). Thermal, UV/vis, and VT-NMR analyses confirmed that PNDITZ-19 K displays photophysical properties and structural integrity indistinguishable from those of Zn-PNDITZ . Charge transport and thermoelectric measurements gave σ ≈ 2 × 10 –2 S cm –1 and a power factor near 1 μW m –1 K –2 . GIWAXS analysis revealed that polymer crystallinity correlates directly with M n / D̵, with PNDITZ-19 K showing the best performance across the series and approaching that of Zn-derived materials. Notably, DARP-synthesized P(NDI2DT-Tz2) achieved a 15-fold reduction in the E -factor (7.23 vs 108.65), highlighting its much lower environmental footprint. These results establish DARP as a sustainable and efficient method for producing high-quality n-type semiconducting polymers.