The Crucial Role of Hydrogen Ligation in the Stability of Single Atoms on Rutile TiO 2 : A First-Principles Study

作者：Sourav Ghoshal, Chidozie Ezeakunne, Yonghyuk Lee, Anastassia N. Alexandrova, Shyam Kattel · 发表于：ACS Applied Materials & Interfaces · 年份：2026 · DOI：10.1021/acsami.5c24310 · 被引用次数：1 · 研究领域：TiO2 Photocatalysis and Solar Cells、Catalytic Processes in Materials Science、Electrocatalysts for Energy Conversion

Understanding the stability of TiO 2 -supported single-atom catalysts (SACs) under H 2 reduction conditions, where hydrogen adsorption on the metal/TiO 2 surface influences metal–support interactions, diffusion, and aggregation, is important for their long-term applications. Using first-principles density functional theory (DFT) calculations, we investigate the thermodynamic and kinetic stability of Rh, Ag, Pt, and Au-based SACs on pristine, oxygen-defective, and hydroxylated rutile TiO 2 (110) surfaces with and without H adsorption on the metal adatom. The thermodynamic driving force for aggregation was assessed by calculating dimerization energies as proxy, while the kinetic stability was quantified in two ways: (i) the total activation energy, E total (E f + E d ), which couples adatom formation (E f ) and diffusion (E d ) energies, serves as a descriptor of ripening kinetics, and (ii) the E d, used to evaluate diffusion rate constants and characteristic diffusion times, τ. The results show that Pt consistently exhibits the largest E total and longest τ, reflecting exceptional resistance to sintering, whereas Ag has the smallest values and is intrinsically unstable. Rh presents a distinctive case: although dimerization is thermodynamically favored, its E total is dominated by the formation energy of two separated Rh atoms on support (*Rh*Rh), giving Rh longer lifetimes than expected from its low diffusion barrier for dimer (*Rh 2 ) formation. Au is unstable on oxygen-defic...