Unlocking Superior Stability in High-Salinity Oxygen Evolution Reaction: A Ru Stabilized NiFeOOH/Ni Anode with over 2000 h Durability

作者：Jun He, Haoyun Sheng, Y. H. Lin, Bingqi Gong, Yayun Zhao, Ziqi Tian, Liang Chen · 发表于：Nano-Micro Letters · 年份：2026 · DOI：10.1007/s40820-026-02072-4 · 被引用次数：3 · 研究领域：Electrocatalysts for Energy Conversion、Ammonia Synthesis and Nitrogen Reduction、Advanced battery technologies research

Abstract Saline water electrolysis presents a promising pathway for green hydrogen production by leveraging abundant saline water resources instead of scarce freshwater. However, the presence of highly corrosive chloride ions (Cl − ) severely undermines anode durability. This instability arises from two main issues: (i) penetration of Cl − through catalyst layers to the underlying substrate and (ii) degradation of active catalytic sites due to Cl − attack. To tackle both issues simultaneously, we introduce ruthenium (Ru) ions as a dual-function stabilizing agent in NiFe-based anodes. Our results show that Ru incorporation promotes the formation of a protective surface layer enriched with Ru atoms, along with a denser NiFeOOH catalyst structure, which collectively inhibit Cl – infiltration. Moreover, atomically dispersed ruthenium (Ru SA ) within the NiFeOOH matrix effectively mitigates Cl – -induced corrosion of active sites. Thanks to this dual stabilization effect, the resulting Ru SA -NiFeOOH/Ni anode exhibits exceptional operational stability—over 2000 h at an industrial current density of 0.5 A cm −2 in a chloride-enriched alkaline medium (1 M KOH + 2 M NaCl)—setting a new benchmark for performance under such aggressive conditions. This study establishes a robust dual stabilization strategy that significantly enhances anode stability in saline water electrolysis.