Effect of Alkali Metal on NH3‐SCR Performance of Fe–Mn/TiO2 Catalyst and Its Mechanism

作者：Lixing Zhang, Lisi Liang, Hongyue Ma, Chen Jin, Yi Li, Zhongyi Cui · 发表于：Chemical Engineering & Technology · 年份：2025 · DOI：10.1002/ceat.70107 · 被引用次数：2 · 研究领域：Catalytic Processes in Materials Science、Nanomaterials for catalytic reactions、Catalysis and Hydrodesulfurization Studies

Abstract The aim of this article is to investigate the effect of alkali metals on the NH 3 ‐SCR performance of Fe–Mn/TiO 2 catalysts and the poisoning mechanism at 30–170 °C. The catalysts without poisoning, with different kinds of alkali metal poisoning, and with different potassium content poisoning were prepared by impregnation method. The activity tests showed that Na, Ca, and K poisoning could lead to different degrees of catalyst deactivation. Characterization analyses showed that alkali metal poisoning decreases the catalyst specific surface area and pore size, reduces the content of surface–active components Mn n + , Fe n + , and (Oα), and reduces the reduction capacity of Mn n + and Fe 3+ . Mechanism analysis showed that K would reduce the reactivity of Lewis acid sites on the catalyst surface, thus leading to a decrease in the intensity of denitrification reactions conducted via the L–H and E–R mechanisms.