Correlating energy density induced residual stress, porosity, and mechanical property variations in directed energy deposition using neutron diffraction and imaging techniques

作者：Chuting Tan, Xinchang Zhang, William Chuirazzi, Cheng Sun, Jeffrey R. Bunn, Yuxuan Zhang, Mario D. Matos, E. Andrew Payzant · 发表于：Journal of Materials Research and Technology · 年份：2025 · DOI：10.1016/j.jmrt.2025.07.284 · 被引用次数：8 · 研究领域：Additive Manufacturing Materials and Processes、Welding Techniques and Residual Stresses、Metal and Thin Film Mechanics

In a directed energy deposition (DED) process, the energy density deposited into the materials drives the structure and properties. The energy density is influenced by several printing parameters, such as laser power, hatch spacing, scanning speed, etc. In this study, 316L stainless steels samples were fabricated with varying hatch spacing aiming to induce variations in sample microstructure and properties. A combination of techniques including engineering neutron diffraction, neutron computed tomography, and tensile testing, were employed to correlate the structure and macroscopic properties. Porosity was predominantly observed at the bottom of the deposited materials and was effectively reduced by decreased hatch spacing. Correlatively, compressive residual stress was observed at the bottom of the specimens, while internal stress is largely determined by the hatch spacing. The residual stress in general decreases as the hatch spacing decreases. The maximum ultimate tensile strength (UTS) was found to increase from 517.4 to 528.6 MPa with a strain increased from 0.847 to 0.897 as the hatch spacing decreased from 0.45 to 0.42 mm. However, further increase in energy density by reducing the hatch spacing resulted in a significant decrease in UTS (as low as 452 MPa). This work provides new insights from bulk non-destructive techniques into correlating energy density induced residual stress, porosity, and mechanical property variations in directed energy deposition.