The Performance of Ti/Steel Joints Welded by Resistance Spot Welding with a Nickel Interlayer

作者：Nannan Wang, Gang Li, Yanling Hu, Hongxin Shi, Ranfeng Qiu, Keke Zhang · 发表于：Materials · 年份：2025 · DOI：10.3390/ma18143247 · 被引用次数：4 · 研究领域：Advanced Welding Techniques Analysis、Titanium Alloys Microstructure and Properties、Intermetallics and Advanced Alloy Properties

Resistance spot welding was performed to join a 2 mm thick TA2 titanium plate and Q235 steel plate using nickel foil with thicknesses of 0.02 mm, 0.04 mm, and 0.06 mm as interlayers. The microstructure of the nugget zone and the interface region of the joint were systematically observed and analyzed, and the tensile shear-bearing capacity of the joint was evaluated. As the welding current increased, the tensile shear load of the joint exhibited a trend of initially increasing and subsequently decreasing. When the welding current was 8 kA, the tensile shear load of the joints with an interlayer of 0.04 mm thickness reached a maximum value of 8.02 kN. The results indicate that employing a reduced welding current can effectively prevent the mixing of nuggets on both sides of the titanium and steel interface. This ensures that the intermetallic compounds formed in the interface region are confined to the Ti-Ni series, which is crucial for enhancing the tensile shear load of the joint.