Low-Crystallinity-Induced Lattice-Distorted Bismuth Nanosheets for Enhanced Electrocatalytic CO 2 Reduction to Formate

作者：Xinxin Zhang, Xiaoyu Liang, Huixin Yan, Xingyan Wang, Xingyan Wang, Yihao Zhang, Min Ji, Min Wang, Xinkui Wang, Xinkui Wang · 发表于：Nano Letters · 年份：2025 · DOI：10.1021/acs.nanolett.5c02163 · 被引用次数：15 · 研究领域：CO2 Reduction Techniques and Catalysts、Advanced Thermoelectric Materials and Devices、Ionic liquids properties and applications

The electrochemical CO 2 reduction reaction (CO 2 RR) to formate offers a sustainable route for carbon neutrality, yet achieving high activity and selectivity remains challenging. Herein, we report a crystallinity-mediated reconstruction strategy to engineer lattice compressive Bi nanosheets for efficient CO 2 electroreduction. Ex situ electrochemical reduction of BOC-L with low crystallinity rapidly forms lattice-distorted Bi nanosheets (Bi NS-L), while BOC-H with high crystallinity undergoes slower reconstruction, yielding ordered Bi nanosheets (Bi NS-H). The compressive strain enhances the CO 2 adsorption and improves the intrinsic activity of Bi nanosheets. Consequently, Bi NS-L achieves a formate Faradaic efficiency of 94.8% at −1.08 V vs RHE, surpassing Bi NS-H (89.1%), with a partial current density of 247.49 mA cm –2 in a flow cell. Moreover, coupling the CO 2 RR with anodic glycerol oxidation (GOR) reduces the cell voltage to 2.3 V (2.5 V for the CO 2 RR/OER) at 200 mA cm –2, enabling 3965.6 μmol h –1 cm –2 formate production.