Uniformly dispersed zinc‐copper alloy as anode preferentially deposited along Zn (002) plane for aqueous zinc ion batteries

作者：Jing Zhu, Longkun Wu, Zhi Peng, Shuo Li, Xudong Li, Zekun Zhang, Ningning Zhao, Bin Li, Meng Wei, Ling Wang, Lei Dai, Zhangxing He · 发表于：Rare Metals · 年份：2025 · DOI：10.1007/s12598-025-03365-0 · 被引用次数：14 · 研究领域：Advanced battery technologies research、Advanced Battery Technologies Research

Abstract Aqueous zinc ion batteries (AZIBs) have attracted widespread attention due to their unique advantages. However, the growth of dendrites on the anode and the occurrence of side reactions limits the improvement of electrochemical performance of AZIBs. The alloying of zinc anode effectively alleviates above problems, which is beneficial to the long‐term cycle performance of AZIBs. In this study, zinc‐copper alloy anode (Cu@Zn) was synthesized by melting method. The method is not only simple and easy to operate, but also can make the synthesized anode Cu element uniform distribution and improve the corrosion resistance of the anode. At the same time, the Cu@Zn surface reconstructed has a large proportion of Zn (002) crystal surface exposure, with the zinc affinity of Cu. Both of them can induce the uniform deposition of Zn 2+ ions along the Zn (002) crystal plane, further inhibiting the growth of dendrite. The Cu@Zn//Cu@Zn symmetrical batteries can cycle more than 1000 times at current densities of 0.3 and 1.2 mA cm −2 , and maintain a relatively low hysteresis voltage. And the discharge capacity retention rate of Cu@Zn//MnO 2 maintains 84.64% at 2.0 A g −1 after 1000 cycles. This study provides a new methodological reference for the development of advanced AZIBs anodes.