Unraveling Atomic-Level Mechanisms of Structural Transitions in Lithium Cobalt Oxide under High-Voltage Conditions

作者：Weiguang Lin, Wei Su, Ting Lin, Qiu Fang, Shiyu Wang, Jing Chen, Y.‐L. He, Dongxiao Wang, Dongdong Xiao, Yingchun Lyu, Qinghua Zhang, Dong Su, Lin Gu · 发表于：Journal of the American Chemical Society · 年份：2025 · DOI：10.1021/jacs.4c17362 · 被引用次数：27 · 研究领域：Advancements in Battery Materials、Advanced Battery Materials and Technologies、Advanced Battery Technologies Research

High-voltage cycling of layered cathode materials in lithium-ion batteries presents challenges related to structural instability. Deciphering atomic-scale structural degradation mechanisms is essential for improving their electrochemical performance at high voltages. This study utilized advanced electron microscopy and principal component analysis to detect subtle spinel-like structure induced by the migration of cobalt atoms within LiCoO 2 subjected to high-voltage cycling at charge voltages of 4.6 and 4.8 V. The formation of the spinel-like configuration was accompanied by the emergence of a densified O1 phase beneath thin spinel-like layer on the (003) facets during charging, along with an intriguing local O3- to P3-type oxygen stacking transition observed in LiCoO 2 charged to 4.8 V. Upon discharge, an enlarged and defective spinel phase preferentially formed on the non-(003) facets, and the migrated cobalt atoms cannot fully return to their original lattice sites, leading to the irreversible structural changes in LiCoO 2 . Long-term cycling revealed that the initial extended spinel phase underwent voltage-dependent evolution pathways, which contributed to accelerated capacity fading observed at the cutoff voltage of 4.8 V. Our findings provide new insights into the atomic-level structural transitions in LiCoO 2 under high-voltage conditions, offering guidance for the development of more structurally robust LiCoO 2 for high-voltage applications.