Low activation Ti30V30Cr5Zr5Ta30-XWX refractory high entropy alloys with excellent mechanical properties and phase stability

作者：Shunhua Chen, Yaocai Tang, Junsheng Zhang, Xiaokang Yue, Haidong Yang, Huohong Tang, Yucheng Wu · 发表于：Intermetallics · 年份：2025 · DOI：10.1016/j.intermet.2025.108780 · 被引用次数：11 · 研究领域：High Entropy Alloys Studies、High-Temperature Coating Behaviors、Additive Manufacturing Materials and Processes

Although refractory high entropy alloys (RHEAs) have the potential to serve as nuclear materials, designing a high-performance alloy that can simultaneously endure extreme environments, such as elevated temperatures and radiation exposure, remains a significant challenge. In this work, elements with high melting points and low activation characteristics are selected to design Ti 30 V 30 Cr 5 Zr 5 Ta 30-x W x (x = 5, 10, 15, 20 at.%) RHEAs that exhibit good high-temperature strength and irradiation resistance. The phase structure, mechanical properties, deformation mechanisms , and irradiation resistance of the RHEAs were investigated and discussed. All the low-activation Ti 30 V 30 Cr 5 Zr 5 Ta 30-x W x RHEAs exhibited excellent phase stability. Typically, the Ti 30 V 30 Cr 5 Zr 5 Ta 15 W 15 RHEA exhibited a yield strength, specific yield strength, and plasticity of 1607 MPa, 172.42 MPa·cm 3 /g and 22.7 % respectively at room temperature. At 800 °C and 1000 °C, it still had a yield strength of 851 MPa and 558 MPa respectively. The high strength of the Ti 30 V 30 Cr 5 Zr 5 Ta 15 W 15 RHEA was attributed to the solid solution strengthening mechanism, in which the W element played an important role. The deformation mechanism of Ti 30 V 30 Cr 5 Zr 5 Ta 15 W 15 RHEA at both room temperature and elevated temperatures was primarily governed by dislocation slip. Using low-energy and high-flux He ions , the irradiation resistance of the Ti 30 V 30 Cr 5 Zr 5 Ta 20 W 10 and Ti 30 V 30 C...