Low‐Ir‐Content Ir 0.10 Mn 0.90 O 2 Solid Solution for Highly Active Oxygen Evolution in Acid Media

作者：Hongyan Hu, Shilong Liu, Hongfei Sun, Wenli Sun, Jian Tang, Lingzhi Wei, Xiaowei Chen, Qianwang Chen, Yichao Lin, Ziqi Tian, Jianwei Su · 发表于：Small · 年份：2025 · DOI：10.1002/smll.202412096 · 被引用次数：16 · 研究领域：Electrocatalysts for Energy Conversion、Fuel Cells and Related Materials、Advanced battery technologies research

Abstract Iridium (Ir)‐based materials are the most widely used oxygen evolution reaction (OER) electrocatalysts in proton exchange membrane water electrolysis (PEMWE). However, their commercial application suffers from high cost and insufficient activity. To optimize the atom utilization efficiency of Ir, the aim is to engineer and develop a rutile‐structured solid solution catalyst with minimal Ir content, which is identified through a phase boundary. Here, Ir 0.10 Mn 0.90 O 2 represents the lowest Ir content in the desired IrO 2 ‐MnO 2 solid solution. The Ir 0.10 Mn 0.90 O 2 catalyst exhibits outstanding OER performance in acidic electrolytes, reaching a remarkable mass activity of 1135 A g −1 Ir at an overpotential of 300 mV, which is ≈50 times higher than that of a commercial IrO 2 catalyst. Additionally, it demonstrates excellent stability at a current density of 200 mA cm −2 over 120 h during PEMWE operations. Density functional theory (DFT) calculations indicate that the hydroxylation process can be efficiently promoted by the electron‐withdrawing on Ir sites in Ir 0.10 Mn 0.90 O 2 , contributing to the enhancement of OER activity.