Small-Sized CsPbI 3 Quantum Dots for High-Performance Pure Red Light-Emitting Diodes

作者：Wenda Yang, Jiaxin Li, Ziyan Cheng, Siyuan Ye, Xue Zhang, Yan Li · 发表于：ACS Applied Energy Materials · 年份：2025 · DOI：10.1021/acsaem.5c00230 · 被引用次数：7 · 研究领域：Perovskite Materials and Applications、Quantum Dots Synthesis And Properties、Optical properties and cooling technologies in crystalline materials

Small-sized CsPbI 3 quantum dots (QDs) are highly promising for fabricating stable pure-red (630–640 nm) light-emitting diodes (LEDs), effectively avoiding the halide segregation issues commonly observed in mixed-halide perovskite nanocrystals. However, synthesizing stable, small-sized colloidal CsPbI 3 QDs for high-efficiency LED fabrication remains a significant challenge. In this study, a combined strategy of metal ion doping and ligand engineering was employed to synthesize small colloidal CsPbI 3 QDs (approximately 5 nm) with pure red emission (630 nm) using the hot injection method. Combined with post-treatment using n -butylammonium iodide (TBAI), the Zn 2+ -doped CsPbI 3 QDs achieved a photoluminescence quantum yield (PLQY) as high as 94% and demonstrated excellent stability, retaining 92% of their initial PL intensity after 80 days of exposure in air. The LED devices fabricated with the obtained CsPbI 3 QDs as emitter layers demonstrated bright electroluminescence at 636 nm with the highest external quantum efficiency value of 10.3%. Furthermore, Zn 2+ -doped CsPbI 3 QDs LEDs also exhibited good operational stability with a half-life of 77 min.