Influence of Ni, Al, W doping on microstructure, corrosion and wear resistance of HVOF spraying Fe-based amorphous alloy coatings

作者：Chengwu Zhang, Lei Xie, Qiang Li, Guan Zhang, Chuntao Chang, Hongxiang Li, Xu Ma, Lin Liu · 发表于：Journal of Materials Research and Technology · 年份：2025 · DOI：10.1016/j.jmrt.2025.01.066 · 被引用次数：17 · 研究领域：Metallic Glasses and Amorphous Alloys、High-Temperature Coating Behaviors、Advanced materials and composites

A series of novel Fe-based amorphous alloy coatings (AACs) with outstanding corrosion and wear resistance, composed of Fe 57 Cr 15 Mo 4 P 10 C 7 B 3 M 4 (M = Fe, Ni, Al and W, in at. %) with various alloying elements, were fabricated using high-velocity oxygen fuel (HVOF) technique. The effect of Ni, Al, and W on microstructure, thermal behavior, corrosion resistance, and wear resistance of these fabricated Fe-based AACs were investigated systematically compared to 316L stainless steel (316L SS) substrates. Microstructural analysis revealed that the present Fe-based AACs exhibited a dense and uniform microstructure with high thermal stability. Electrochemical test results demonstrated that doping with Ni, Al and W significantly enhanced the corrosion resistance of the base alloy AAC. The W-doped AAC showed the best performance than Ni-doped, Al-doped and base alloy AAC, with a wide passive region (Δ E pass ) of 1.7 V, low self-corrosion current density ( I corr ) of 1.07 ×10 -6 A·cm -2 and the lowest steady-state current densities and highest passivation index. Mott–Schottky analysis and X-ray photoelectron spectroscopy results showed that the W-doped AACs forming the densest and thickest passivation films, ascribed to an increased fraction of protective and stable low-valent metal oxides (Fe 2+ /Cr 3+ /Mo 4+ ), enhanced corrosion resistance by promoting film growth and degradation processes. Dry wear tests revealed that among these Fe-based AACs, the W-doped AAC exhibited th...