Photochromic Film Based on a Mixed-Heteroatom-Templated Er III -Incorporated Polyoxometalate Used for Inkless Prints and Anti-Counterfeiting

作者：Yanan Chen, Tiantian Gong, Qiuxia Han, Jiancai Liu, Lijuan Chen, Junwei Zhao · 发表于：ACS Applied Materials & Interfaces · 年份：2024 · DOI：10.1021/acsami.4c19437 · 被引用次数：18 · 研究领域：Polyoxometalates: Synthesis and Applications、Photochromic and Fluorescence Chemistry、Sulfur-Based Synthesis Techniques

Photochromic films have attracted increasing attention for their potential in information storage and photoswitchable devices. Developing novel photochromic materials is still a highly challenging topic. In this work, we successfully obtained an unprecedented mixed-heteroatom-templated Er III -incorporated polyoxometalate [H 2 N(CH 3 ) 2 ] 18 Na 2 K 2 H 12 {Er 2 (H 2 O) 10 W 14 O 43 [SeTeW 15 O 54 ][B-α-TeW 9 O 33 ] 2 } 2 ·117H 2 O ( 1 ) by concurrently introducing the [TeO 3 ] 2– and [SeO 3 ] 2– heteroanion templates into the Er 3+ /WO 4 2– system. The most attractive feature is that this polyoxoanion of 1 consists of three kinds of polyoxometalate building units such as classical trivacant Keggin [B-α-TeW 9 O 33 ] 8–, rarely seen trivacant Te IV –Se IV -oriented Dawson-like [SeTeW 15 O 54 ] 10–, and extraordinary [W 14 O 43 ] 2– with an infrequent [W VI O 7 (W VI 5 O 20 )] 18– pentagon subunit. Based on the photochromism feature of polyoxometalates in the presence of organic electron donors under light irradiation, a photochromic composite film GEL/TEG/ 1 was fabricated by mixing 1 with gelatin (GEL) and triethylene glycol (TEG). The GEL/TEG/ 1 film shows good photochromic properties under 365 nm UV irradiation. The film changed color within 15 min under UV irradiation. The photochromic properties endow the film with fast and easy “‘printing’” performance. The “printed” text or pattern in the film can be erased within 35 h in an atmospheric environment at room temperature, ...