Synergistic effects of CO2 and H2S on stress corrosion cracking of stainless steel 254SMo in extremely aggressive oilfield environment

作者：Song Meng, Penghui Yue, Shucai Zhang, Huabing Li, Yang Zhao, Yong Hua, Tao Zhang, Fuhui Wang · 发表于：Corrosion Communications · 年份：2024 · DOI：10.1016/j.corcom.2024.03.003 · 被引用次数：39 · 研究领域：Hydrogen embrittlement and corrosion behaviors in metals、Corrosion Behavior and Inhibition、Non-Destructive Testing Techniques

Synergistic effects of CO 2 and H 2 S on stress corrosion cracking of stainless steel 254 SMo in extremely aggressive oilfield environments were explored through experiments and water chemistry modelling calculations. Fracture morphology reveals transition from ductile fracture to plastic fracture characteristics. Initiation of fracture was attributed to pitting corrosion, and depth of the pits was consistent with the Gumbel distribution. Presence of CO 2 and H 2 S exhibits a coupling effect on stress corrosion cracking of stainless steel 254 SMo. Ionization of H 2 S promoted by CO 2 produced more HS − and S 2− with increasing temperature and pressure, accelerated pit generation on the surface, and increased susceptibility to stress corrosion cracking.