Laser powder bed fusion of GH4099 Ni-based superalloy under a static magnetic field with tailored microstructure and enhanced mechanical performance

作者：Chaoyue Chen, Keqing Zhang, Ruixin Zhao, Songzhe Xu, Tao Hu, Xia Li, Xiaopeng Li, Linda Ke, Jiang Wang, Zhongming Ren · 发表于：Virtual and Physical Prototyping · 年份：2024 · DOI：10.1080/17452759.2024.2411023 · 被引用次数：19 · 研究领域：Additive Manufacturing Materials and Processes、High Entropy Alloys Studies、Additive Manufacturing and 3D Printing Technologies

In the present work, the static magnetic field (SMF) was applied in the L-PBF process of a typical γʹ strengthening Ni-based superalloy of GH4099 concerning the as-built and heat-treated conditions. The SMF during the L-PBF process can effectively refine the cellular str ucture, refine the grain size, promote the columnar to equiaxed transition (CET), and reduce the dislocation density. After the solution-aging procedure, the SMF samples exhibited a refined grain structure, suggesting that the tailored microstructure is inherited after the solution-aging treatment. The tensile test results show that by applying the SMF during the L-PBF process, the ductility can be notably improved on both building planes under the as-built and heat-treatment conditions, and the anisotropy along different directions can be reduced. It reveals that the SMF in L-PBF can be an effective method to modulate the microstructure and improve the comprehensive mechanical properties for γʹ strengthening Ni-based superalloys.