作者：Ziqing Yin, Yufeng Mao, Shikao Shi, Jiye Wang, Ruilong Zong · 发表于：Journal of Advanced Ceramics · 年份：2024 · DOI：10.26599/jac.2024.9220982 · 被引用次数：22 · 研究领域：Luminescence Properties of Advanced Materials

Red-light-emitting phosphors capable of being well excited with blue light are highly desirable in solid-state lighting. In this work, a novel Eu3+-activated high-entropy rare earth oxide Ce0.2La0.2Gd0.2Y0.2Lu0.2O1.6:xEu3+ (x = 4–16 mol%) phosphor was successfully prepared by solution combustion reaction for the first time. The multi-composition rare earth oxide has a specific cubic fluorite structure, which is almost the same as that of the pure CeO2 despite the tiny ceria composition in the sample, demonstrating the formation of a high-entropy composite solid solution. To our surprise, the high-entropy phosphor exhibits extremely intense red emission at 613 nm, corresponding to the 5D0→7F2 characteristic transition of Eu3+ under the excitation of blue light at 466 nm. The luminescence internal quantum yield (QY) for the optimal high-entropy phosphor (x = 12 mol%) reaches nearly 50% and can further increase to 67.8% through a subsequent heat-treatment process at 1400 °C. The QY result is much superior to that of previously reported Eu3+-activated CeO2 as well as Y2Ce2O7 and La2Ce2O7 low-entropy composite oxides (QYs are approximately 10%–20%). Moreover, the high-entropy oxide phosphor also shows better luminescence thermal stability than low-entropy oxides, as confirmed from the temperature-dependent photoluminescence emission spectra. The tremendous improvement in optical properties depends closely upon the high-entropy and other related effects. The novel high-entropy rare...