De‐Passivation and Surface Crystal Plane Reconstruction via Chemical Polishing for Highly Reversible Zinc Anodes

作者：Jin Cao, Xu Wang, Shangshu Qian, Dongdong Zhang, Ding Luo, Lulu Zhang, Jiaqian Qin, Xinyu Zhang, Xuelin Yang, Jun Biao Lu · 发表于：Advanced Materials · 年份：2024 · DOI：10.1002/adma.202410947 · 被引用次数：149 · 研究领域：Advanced battery technologies research、Perovskite Materials and Applications、Advanced Battery Materials and Technologies

Abstract Despite the widespread adoption of Zn anodes for aqueous energy storage, the presence of an inherent passivation layer and the polycrystalline interface of commercial Zn foil consistently lead to non‐uniform electrodeposition, undermining stability and practicality. Herein, the study introduces a chemically polished Zn metal anode (CP‐Zn) fabricated via a simple immersion method. This “chemically polishing” process can effectively remove the interfacial passivation layer (de‐passivation), providing ample active sites for plating/stripping and ensuring the uniformly distributed electric field and Zn 2+ ion flux. Additionally, selective etching during chemical polishing exposes more (002) crystal planes, promoting homogeneous and smooth zinc deposition while suppressing related side reactions. Demonstrated by CP‐Zn anode, the symmetric cell exhibits stable cycling over 4600 h at 1 mA cm −2 and 240 h at 50% depth of discharge (DOD), with a CP‐Zn||VO 2 full cell maintaining ≈75.3% capacity retention over 1000 cycles at 3 A g −1 . This chemically polishing strategy presents a promising avenue for advancing the commercialization of aqueous zinc‐ion batteries.