Chemically Bonded Biphase Coating of Ni-Rich Layered Oxides with Enhanced High-Voltage Tolerance and Long-Cycle Stability

作者：Mohan Yang, Danhua Li, Jing Wang, Hanlou Li, Ran Wang, Qi Liu, Meng Wang, Feng Wu, Fang Wang, Guoqiang Tan · 发表于：ACS Applied Materials & Interfaces · 年份：2024 · DOI：10.1021/acsami.4c11143 · 被引用次数：9 · 研究领域：Transition Metal Oxide Nanomaterials、Advancements in Battery Materials、Semiconductor materials and devices

Stabilizing the crystalline structure and surface chemistry of Ni-rich layered oxides is critical for enhancing their capacity output and cycle life at a high cutoff voltage. Herein, we adopted a simple one-step solid-state method by directly sintering the Ni 0.9 Co 0.1 (OH) 2 precursor with LiOH and Ta 2 O 5, to simultaneously achieve the bulk material synthesis of LiNi 0.9 Co 0.1 O 2 and in situ construction of a rock-salt Ta-doped interphase and an amorphous LiTaO 3 outer layer, forming a chemically bonded surface biphase coating on LiNi 0.9 Co 0.1 O 2 . Such a cathode architectural design has been demonstrated with superior advantages: (1) eliminating surface residual alkali, (2) strengthening the layered oxygen lattice, (3) suppressing bulk-phase transformation, and (4) facilitating Li-ion transport. The obtained cathode exhibits excellent electrochemical performance, including a high initial reversible capacity of 180.3 mAh g –1 at 1.0 C with 85.5% retention after 300 cycles (2.8–4.35 V) and a high initial reversible capacity of 182.5 mAh g –1 at 0.2 C with 87.6% retention after 100 cycles (2.8–4.5 V). Notably, this facile and scalable electrode engineering makes Ni-rich layered oxides promising for practical applications.