A FeCrAl-Al2O3 Composite Produced Via Laser Powder Bed Fusion of a Mixed Powder for Porous Catalyst Scaffolds

作者：Kwangtae Son, Hsin-Mei Kao, Patrick S. McNeff, Seongun Yang, Nahal Ghanadi, Somayeh Pasebani, Chi-hung Chang, Brian K. Paul · 发表于：Journal of Micro and Nano-Manufacturing · 年份：2024 · DOI：10.1115/1.4066114 · 被引用次数：2 · 研究领域：Additive Manufacturing Materials and Processes、Bone Tissue Engineering Materials、Additive Manufacturing and 3D Printing Technologies

Abstract This study proposes a novel approach for synthesizing and etching bicontinuous FeCrAl-Al2O3 composites as a means for replacing FeCrAl foams as catalyst scaffolds in biodriven alcohol reactors for jet-fuel production. Conventional FeCrAl foams suffer from poor availability and consequent high costs. New additive manufacturing techniques provide an opportunity to produce tailored foams at reasonable times and at acceptable costs. This research aimed to generate a porous FeCrAl structure by etching a bicontinuous FeCrAl-Al2O3 composite produced by laser powder bed fusion of amalgamated FeCrAl and Al2O3 powders. The composite powder for laser powder bed fusion is created by ball-milling FeCrAl and Al2O3 powders. This research focuses on achieving a bi-continuous FeCrAl-Al2O3 structure, essential for the selective removal of the ceramic phase. The influence of laser processing parameters on the microstructure was examined across a range of laser powers (60–120 W) and scan speeds (100–400 mm/s), showing that higher powers and speeds produce finer metal struts. A bi-continuous microstructure was consistently obtained, marking a key achievement. The Al2O3 removal process involved a two-step etching method using hydrochloric and phosphoric acids, tested across various etching times. The alumina phase was reduced from 36 vol% to 17 vol% (corresponding to an increase in porosity from 24 vol% to 43 vol%), showing the potential for use as a porous catalyst scaffold. This researc...