Investigation and Utilization of Alkali-Activated Grouting Materials Incorporating Engineering Waste Soil and Fly Ash/Slag

作者：Zhijia Wang, Haojie Li, Shusu Duan, Zhisheng Feng, Youliang Zhang, Jianjing Zhang · 发表于：Applied Sciences · 年份：2024 · DOI：10.3390/app14114915 · 被引用次数：11 · 研究领域：Grouting, Rheology, and Soil Mechanics、Concrete and Cement Materials Research、Electrokinetic Soil Remediation Techniques

The alkali-activated composites technique is a promising method for the in situ preparation of cavity filling/grouting materials from engineering waste soil. To investigate the feasibility of engineering waste soil utilization by the alkali activation process, the macroscopic and microscopic properties of the fly ash/slag-based alkali-activated composites, after solidification/stabilization (S/S) with sandy clay excavated at Baishitang Station of Shenzhen Metro, were studied. The unconfined compressive strength (UCS) test was conducted to evaluate the S/S effect of alkali-activated composites. The results show that the optimum quality ratio of slag and fly ash correspond to 7:3, the modulus of alkaline activator to 1.3, and the alkalinity of alkaline activator to 10%. The alkali-activated composite’s strength under these parameters can reach 45.25 MPa at 3 days, 49.85 MPa at 7 days, and 62.33 MPa at 28 days. A maximum 3-day UCS of 21.71 MPa, 75% of the 28-day UCS, was achieved by an engineering waste soil and alkali-activated composites mass ratio of 5:5, slaked lime content of 4.5%, and a water-to-solid ratio of 0.26, and it can also meet the required fluidity and setting time for construction well. Fluidity is primarily affected by the soil-to-binder ratio, which decreases as the ratio decreases, while the water-to-solid ratio increases fluidity. Slaked lime has minimal impact on fluidity. The setting time is mainly influenced by the soil-to-binder ratio, followed by slaked...