Chloride Corrosion Process of Concrete with Different Water–Binder Ratios under Variable Temperature Drying–Wetting Cycles

作者：Lei Wang, Chunhong Chen, Ronggui Liu, Pinghua Zhu, Hui Liu, Jiang Hong-wei, Jiang Yu · 发表于：Materials · 年份：2024 · DOI：10.3390/ma17102263 · 被引用次数：8 · 研究领域：Concrete and Cement Materials Research、Concrete Corrosion and Durability、Magnesium Oxide Properties and Applications

In this paper, four water-binder ratios (w/b) of 0.29, 0.33, 0.39, and 0.46 were designed. A variable test temperature was implemented in the drying-wetting cycle test according to the temperature fluctuations in the actual service environment, and the constant temperature test was established as the control group. The mechanical properties and chloride corrosion resistance of concrete with different w/b ratios under variable temperature drying-wetting cycles, as well as the microstructure changes, phase composition, and damage mechanism inside the concrete, were investigated. The results showed that the mechanical properties of concrete increased first and then decreased with drying-wetting cycles increasing, whereas the chloride corrosion resistance continued to decline. A higher w/b exacerbated the deterioration of the concrete performance. A higher w/b increased the porosity, chloride diffusion depth, and chloride content, thus reducing the resistance of chloride corrosion. Compared with w/b = 0.29, the compressive strength, splitting tensile strength, mass, and relative dynamic elasticity modulus of w/b = 0.46 exposed to 60 drying-wetting cycles decreased by 54.50%, 52.44%, 0.96%, and 6.50%, respectively, while the porosity, peak chloride content, and erosion depth increased by 45.12%, 70.45%, and 45.00%. Compared with the drying-wetting cycle with a constant temperature, the cumulative damage caused by the drying-wetting cycle with a variable temperature was greater, re...