Special texture evolution behavior of strip-cast non-oriented electrical steel combined with in-situ experiment and CPFEM

作者：Jiale Wang, Chao Sun, Junjie Wang, Feng Fang, Yuanxiang Zhang, Yang Wang, Guangming Cao, Xiaoming Zhang, Guo Yuan, Guodong Wang · 发表于：Journal of Materials Research and Technology · 年份：2024 · DOI：10.1016/j.jmrt.2024.04.029 · 被引用次数：9 · 研究领域：Magnetic Properties and Applications、Microstructure and Mechanical Properties of Steels、Microstructure and mechanical properties

The impact of shear deformation on texture evolution in strip-cast Fe-1.5%Si non-oriented electrical steel was studied combined with in-suit experiments and crystal plasticity finite element method (CPFEM). Throughout the deformation process, the texture evolution predominantly follows a traditional route: transitioning from {211}<036> and {411}<148> to {111}<112> orientation. In certain regions with specific stress conditions, orientation evolution shifts from {310}<236> to {411}<148>, {100}<021>, and finally to {100}<001> orientation. Crystal plasticity finite element (CPFE) simulation results show that the rotation of {310}<236> through {411}<148> to {100}<021> orientation, {211}<236> and {112}<110> orientations transition to {111} and {110} orientations, respectively, which is consistent with the experimental observations. Recrystallization texture mainly includes favorable λ and near-λ (<100>∥ND, normal direction) textures, with detrimental γ (<111>∥ND) texture essentially diminishing. In-situ heating experiments revealed {411}<148> as the primary recrystallization orientation, the mechanism involves both oriented nucleation and growth. In the edge region lacking stress constraints, the Schmid factor (SF) reaches up to 0.48, the (21-3)[111] slip system is preferentially activated, with shear bands appearing earlier in the same region. Indicating that when slip mechanism alone are inadequate for sustaining plastic deformation, the shear deformation becomes the favored mod...