Effect of temperature and moisture composite environments on the mechanical properties and mechanisms of woven carbon fiber composites

作者：Jingsong Chen, Guangwu Yang, Shoune Xiao, Dongdong Chen, Mingmeng Wang, Lanxin Jiang · 发表于：Polymer Composites · 年份：2024 · DOI：10.1002/pc.28085 · 被引用次数：16 · 研究领域：Mechanical Behavior of Composites、Fiber-reinforced polymer composites、Natural Fiber Reinforced Composites

Abstract Temperature and moisture are important environmental conditions governing the usage of carbon fiber‐reinforced plastics (CFRP). In this study, tensile, compression, and shear tests of woven CFRP composites were conducted in four composite environments: cold‐temperature dry state, room‐temperature dry state, elevated‐temperature dry state, and elevated‐temperature wet state. Fourier transform infrared (FTIR) spectroscopy was used to analyze the molecular composition and structure under these environments. The fracture morphology was also analyzed using scanning electron microscopy (SEM) to understand the deterioration mechanism of the material properties at the macro and micro scales. Finally, a two‐parameter Weibull statistical model was used to evaluate the scattering of the composites. The results demonstrate that the tensile, compressive, and shear properties of the material decrease under harsh conditions, and the degradation effect on the ultimate strength is much greater than that of the modulus. Cold‐temperature dry and elevated‐temperature wet conditions are particularly severe. Composite environments significantly affect the macroscopic failure process and ultimate failure mode of materials. In general, the temperature and humidity of the matrix system acts at the core of the deterioration mechanism of composites, affecting the properties of the fiber/matrix and orthogonal woven fiber interfaces, and eventually resulting in a loss of their constitutive stren...