In situ observation of melt pool evolution in ultrasonic vibration-assisted directed energy deposition

作者：Salma A. El-Azab, Cheng Zhang, Sen Jiang, Aleksandra L. Vyatskikh, Lorenzo Valdevit, Enrique J. Lavernia, Julie M. Schoenung · 发表于：Scientific Reports · 年份：2023 · DOI：10.1038/s41598-023-44108-4 · 被引用次数：36 · 研究领域：Additive Manufacturing Materials and Processes、Additive Manufacturing and 3D Printing Technologies、Welding Techniques and Residual Stresses

The presence of defects, such as pores, in materials processed using additive manufacturing represents a challenge during the manufacturing of many engineering components. Recently, ultrasonic vibration-assisted (UV-A) directed energy deposition (DED) has been shown to reduce porosity, promote grain refinement, and enhance mechanical performance in metal components. Whereas it is evident that the formation of such microstructural features is affected by the melt pool behavior, the specific mechanisms by which ultrasonic vibration (UV) influences the melt pool remain elusive. In the present investigation, UV was applied in situ to DED of 316L stainless steel single tracks and bulk parts. For the first time, high-speed video imaging and thermal imaging were implemented in situ to quantitatively correlate the application of UV to melt pool evolution in DED. Extensive imaging data were coupled with in-depth microstructural characterization to develop a statistically robust dataset describing the observed phenomena. Our findings show that UV increases the melt pool peak temperature and dimensions, while improving the wettability of injected particles with the melt pool surface and reducing particle residence time. Near the substrate, we observe that UV results in a 92% decrease in porosity, and a 54% decrease in dendritic arm spacing. The effect of UV on the melt pool is caused by the combined mechanisms of acoustic cavitation, ultrasound absorption, and acoustic streaming. Throug...