Enhanced laser-induced damage performance of all-glass metasurfaces for energetic pulsed laser applications

作者：Nathan J. Ray, Jae‐Hyuck Yoo, Hoàng Tùng Nguyễn, Mary A. Norton, David A. Cross, Christopher W. Carr, Eyal Feigenbaum · 发表于：Applied Optics · 年份：2023 · DOI：10.1364/ao.502242 · 被引用次数：11 · 研究领域：Laser Material Processing Techniques、Optical Coatings and Gratings、Surface Roughness and Optical Measurements

To fabricate optical components with surface layers compatible with high-power laser applications that may operate as antireflective coatings, polarization rotators, or harness physical anisotropy for other uses, metasurfaces are becoming an appealing candidate. In this study, large-beam (1.05 cm diameter) 351-nm laser-induced damage testing was performed on an all-glass metasurface structure composed of cone-like features with a subwavelength spacing of adjacent features. These structures were fabricated on untreated fused silica glass and damage tested, as were structures that were fabricated on fused silica glass that experienced a preliminary etching process to remove the surface Beilby layer that is characteristic of polished fused silica. The laser-induced damage onset for structures on untreated fused silica glass was 19.3J⋅cm −2 , while the sample that saw an initial pretreatment etch exhibited an improved damage onset of 20.4J⋅cm −2 , only 6% short of the reference pretreated glass damage onset of 21.7J⋅cm −2 . For perspective, the National Ignition Facility operational average fluence at this wavelength and pulse length is about 10J/cm 2 . At a fluence of 25.5J⋅cm −2 , the reference (pretreated) fused silica initiated 5.2 damage sites per mm 2 , while the antireflective metasurface sample with a preliminary etching process treatment initiated 9.8 damage sites per mm 2 . These findings demonstrate that substrate-engraved metasurfaces are compatible with high energy a...