The microstructure and He+ ion irradiation behavior of novel low-activation W-Ta-Cr-V refractory high entropy alloy for nuclear applications

作者:Damian Kalita, I. Jóźwik, Ł. Kurpaska, Yanwen Zhang, K. Mulewska, Witold Chromiński, J.H. O’Connell, Yanling Ge, Walker L. Boldman, Philip D. Rack, Yongqiang Wang, William J. Weber, J. Jagielski · 发表于:Nuclear Materials and Energy · 年份:2023 · DOI:10.1016/j.nme.2023.101513 · 被引用次数:35 · 研究领域:High Entropy Alloys Studies、Nuclear Materials and Properties、Advanced materials and composites

Microstructure and nanohardness of a nearly equimolar W-Ta-Cr-V high entropy alloy (HEA), as well as its irradiation response under He+ irradiation, were investigated. The single-phase body-centered cubic nanostructured alloy with a 1 µm thick layer was fabricated on a silicon substrate using a magnetron sputtering method. The HEA film has a complex microstructure consisting of micrometric domains that exhibit internal nanostructure controlled by their crystal orientation. The measured nanohardness of the W-Ta-Cr-V alloy is 13±2 GPa, which significantly exceeds the hardness of nanocrystalline tungsten as a result of the high solid-solution strengthening effect. In order to evaluate the irradiation resistance of the HEA film, the material was irradiated with 200 keV He+ ions at room temperature, with two different ion fluences: 1×1016 and 5×1016 ions/cm2. Using transmission electron microscopy, a high density of extremely fine He bubbles is observed that were uniformly distributed in the matrix. The increase of He+ ion fluence increased the density of bubbles, whereas their size remained at a similar level, which indicates that the damage proceeds by the nucleation of additional He bubbles, not by their growth.