Low‐Dimensional 2‐thiopheneethylammonium Lead Halide Capping Layer Enables Efficient Single‐Junction Methylamine‐Free Wide‐Bandgap and Tandem Perovskite Solar Cells

作者：Hongling Guan, Wenjun Zhang, Jiwei Liang, Chen Wang, Xuzhi Hu, Dexing Pu, Lishuai Huang, Yansong Ge, Hongsheng Cui, Yuanrong Zou, Guojia Fang, Weijun Ke · 发表于：Advanced Functional Materials · 年份：2023 · DOI：10.1002/adfm.202300860 · 被引用次数：45 · 研究领域：Perovskite Materials and Applications、Quantum Dots Synthesis And Properties、Conducting polymers and applications

Abstract Wide‐bandgap (WBG) perovskite solar cells (PSCs) have garnered significant attention for their potential applications in tandem solar cells. However, their large open‐circuit voltage ( V OC ) deficit and serious photo‐induced halide segregation remain the main challenges that impede their applications. Herein, a post‐treatment strategy without thermal annealing is presented to form a 2D top layer of 2‐thiopheneethylammonium lead halide ( n = 1) on WBG perovskites. This thermal annealing‐free post‐treatment method can more effectively passivate the defects of WBG methylamine (MA)‐free formamidinium/cesium lead iodide/bromide perovskite films and suppress photo‐induced perovskite phase segregation, as compared with the thermal annealing method that yields multi‐2D phases. The resulting opaque and semi‐transparent 1.66 eV‐bandgap perovskite solar cells deliver maximum power conversion efficiencies of 21.47% (a small V OC deficit of 0.43 V) and 19.11%, respectively, both of which are among the highest reports for inverted MA‐free WBG PSCs. Consequently, four‐terminal all‐perovskite tandem cells realize a remarkable efficiency of 26.64%, showing great promise for their applications in efficient multi‐junction tandem solar cells.