Electrolyte Solvation Engineering toward High-Rate and Low-Temperature Silicon-Based Batteries

作者：Zhang Cao, Xueying Zheng, Mi Zhou, Tong Zhao, Linze Lv, Yuchen Li, Zhongqiang Wang, Wei Luo, Honghe Zheng · 发表于：ACS Energy Letters · 年份：2022 · DOI：10.1021/acsenergylett.2c01840 · 被引用次数：104 · 研究领域：Advancements in Battery Materials、Advanced Battery Materials and Technologies、Supercapacitor Materials and Fabrication

Silicon (Si)-based batteries can only work in a narrow temperature range, where their subzero operation has been severely hampered by the sluggish charge transfer and ion diffusion processes. In overcoming such kinetic barriers, a weakly solvating electrolyte is tailored herein, which bypasses the Li + desolvation difficulties by its fluorinated structure that lowers the Li + solvating capability. Specifically, our recipe is based on 1 M LiFSI in fluoroethylene carbonate (FEC)/bis(2,2,2-trifluoroethyl) carbonate (BTFC) solvents. Additional incorporation of poor-solvating ethyl trifluoroacetate (ETFA) cosolvent further weakens the electrolyte solvation power, while efficaciously lowering the electrolyte viscosity and melting point. Such a combination affords prolonged Si cyclability for 200 cycles at RT (capacity-decay rate of 0.0945% per cycle). Even at −20 °C, the Si electrode still delivers a discharge capacity as high as 2005.7 mAh g –1 that proceeds for 200 cycles. Pairing with a commercial LiNi 0.5 Co 0.2 Mn 0.3 O 2 cathode, the full cell affords a capacity of 104.6 mAh g –1 when being charged/discharged at −20 °C, which presented quite stable performance over 100 cycles.