Diatomite Composited with a Zeolitic Imidazolate Framework for Removing Phosphate from Water

作者：Zicheng Chen, Huiwen Zhang, Guangyuan Fan, Xiangyang He, Zhibin He, Lanhe Zhang · 发表于：ACS Omega · 年份：2022 · DOI：10.1021/acsomega.2c01648 · 被引用次数：16 · 研究领域：Phosphorus and nutrient management、Adsorption and biosorption for pollutant removal、Layered Double Hydroxides Synthesis and Applications

Adsorption technology based on various adsorbents has been widely applied in wastewater treatment containing phosphate. A novel diatomite adsorbent composited with ZIF-8 (CZD) was developed for removing phosphate from water in this work. The chitosan was used to pre-modify the diatomite so that ZIF-8 could be anchored on the surface of the diatomite solidly and uniformly. The diatomite composited with ZIF-8 was then used to remove phosphate in water by an adsorption process, the process variables such as adsorption time, temperature, pH, and competitive ions were investigated. The electrostatic attraction was the primary mechanism of phosphate removal. The adsorption reached equilibrium within 90 min, and its sorption capacity increased when adsorption time and temperature increased. Especially, CZD had a rapid adsorption rate and 85% of the phosphate in the solution can be adsorbed within the first 10 min. The maximum phosphate adsorption capacities of the modified diatomite reached 13.46, 13.55, and 13.95 mg/g at 25, 35, and 45 °C, respectively. The removal efficiencies of CZD for phosphate were more than 98% and even came up to 100% at 45 °C. The adsorption isotherms fit well with the Langmuir isotherm model. The Freundlich isotherm and Temkin isotherm showed that the adsorption process is physical in nature. The kinetic data of the adsorption process were fitted by the pseudo-second-order kinetics. Thermodynamic parameters indicated that the adsorption process was endothe...