Activating Oxygen Redox in Layered NaxMnO2 to Suppress Intrinsic Deficient Behavior and Enable Phase‐Transition‐Free Sodium Ion Cathode

作者：Feng Wang, Bo Peng, Suyuan Zeng, Liping Zhao, Xiaolei Zhang, Guanglin Wan, Hongli Zhang, Genqiang Zhang · 发表于：Advanced Functional Materials · 年份：2022 · DOI：10.1002/adfm.202202665 · 被引用次数：95 · 研究领域：Advancements in Battery Materials、Advanced Battery Materials and Technologies、Multiferroics and related materials

Abstract P2‐type layered NaxMnO2 cathode shows great potential in practical sodium ion batteries, especially for grid‐level applications due to its eco‐friendly and cost‐effective sodium and manganese resources, and high theoretical specific capacity. However, several obstacles including severe phase transitions of P2‐O2 and P2‐P2′, low redox potential of Mn3+/Mn4+, disproportionation reaction and Jahn‐Teller distortion of Mn3+, and deficient behavior have already hindered its practical applications. Herein, a Li, Cu co‐doping strategy to tackle the mentioned obstacles by activating the oxygen redox is presented. The Li, Cu co‐doped material exhibits solid solution reaction without any phase transitions as proved by in situ X‐ray diffraction measurement and reduces the dissolution of active manganese element. With this modification treatment, it can dramatically raise the cycling stability from 30.4% to 80.1% after 150 cycles and simultaneously improves the deficient behavior due to the capacity contribution of oxygen redox at high voltage. More importantly, the coin‐cell type sodium ion full cell assembled with this cathode and commercial hard carbon anode delivers a promising energy density of 225.1 Wh kg–1.