MIL‐100(Fe) Supported Pt−Co Nanoparticles as Active and Selective Heterogeneous Catalysts for Hydrogenation of 1,3‐Butadiene

作者：Lili Liu, Zhixuan Han, Yifan Lv, Chunling Xin, Xiaojing Zhou, Lei Yu, Xi–Shi Tai · 发表于：ChemistryOpen · 年份：2022 · DOI：10.1002/open.202100288 · 被引用次数：21 · 研究领域：Metal-Organic Frameworks: Synthesis and Applications、Catalysis for Biomass Conversion、Catalysis and Hydrodesulfurization Studies

Superior catalytic performance for selective 1,3-butadiene (1,3-BD) hydrogenation can usually be achieved with supported bimetallic catalysts. In this work, Pt-Co nanoparticles and Pt nanoparticles supported on metal-organic framework MIL-100(Fe) catalysts (MIL=Materials of Institut Lavoisier, PtCo/MIL-100(Fe) and Pt/MIL-100(Fe)) were synthesized via a simple impregnation reduction method, and their catalytic performance was investigated for the hydrogenation of 1,3-BD. Pt1Co1/MIL-100(Fe) presented better catalytic performance than Pt/MIL-100(Fe), with significantly enhanced total butene selectivity. Moreover, the secondary hydrogenation of butenes was effectively inhibited after doping with Co. The Pt1Co1/MIL-100(Fe) catalyst displayed good stability in the 1,3-BD hydrogenation reaction. No significant catalyst deactivation was observed during 9 h of hydrogenation, but its catalytic activity gradually reduces for the next 17 h. Carbon deposition on Pt1Co1/MIL-100(Fe) is the reason for its deactivation in 1,3-BD hydrogenation reaction. The spent Pt1Co1/MIL-100(Fe) catalyst could be regenerated at 200 °C, and regenerated catalysts displayed the similar 1,3-BD conversion and butene selectivity with fresh catalysts. Moreover, the rate-determining step of this reaction was hydrogen dissociation. The outstanding activity and total butene selectivity of the Pt1Co1/MIL-100(Fe) catalyst illustrate that Pt-Co bimetallic catalysts are an ideal alternative for replacing mono-noble-metal...