Variable amplitude very high cycle fatigue of 17-4PH steel with a stepwise S-N curve

作者：Bernd M. Schönbauer, M. Fitzka, Ulrike Karr, H. Mayer · 发表于：International Journal of Fatigue · 年份：2020 · DOI：10.1016/j.ijfatigue.2020.105963 · 被引用次数：25 · 研究领域：Fatigue and fracture mechanics、Fire effects on concrete materials、High Temperature Alloys and Creep

High and very high cycle fatigue (VHCF) tests were performed with 17-4PH stainless steel under constant amplitude (CA) and variable amplitude (VA) loading at load ratios of −1 and 0.05. Stepwise (duplex) S-N curves were determined with failure from surface inclusions above the transition stress amplitude, σtr, and from the interior below σtr. Similar σtr for CA and VA loading were found. VA failure occurred at Miner damage sums between 0.1 and 0.9 (surface failure) and 0.2 and 2.2 (internal failure). Omission of stress amplitudes less than 60% of the maximum amplitude is allowable for VA studies in the VHCF regime.