Mechanical property and reliability of bimodal nano-silver paste with Ag-coated SiC particles

作者：Qiaoran Zhang, Abdelhafid Zehri, Jiawen Liu, Wei Ke, Shirong Huang, Martí Gutierrez Latorre, Nan Wang, Xiuzhen Lu, Cheng Zhou, Weijuan Xia, Yanpei Wu, Lilei Ye, Johan Liu · 发表于：Soldering and Surface Mount Technology · 年份：2019 · DOI：10.1108/ssmt-05-2018-0014 · 被引用次数：28 · 研究领域：Aluminum Alloys Composites Properties、Electronic Packaging and Soldering Technologies、Advanced ceramic materials synthesis

Purpose This study aims to develop a bimodal nano-silver paste with improved mechanical property and reliability. Silicon carbide (SiC) particles coated with Ag were introduced in nano-silver paste to improve bonding strength between SiC and Ag particles and enhance high-temperature stability of bimodal nano-silver paste. The effect of sintering parameters such as sintering temperature, sintering time and the proportion of SiC particles on mechanical property and reliability of sintered bimodal nano-silver structure were investigated. Design/methodology/approach Sandwich structures consist of dummy chips and copper substrates with nickel and silver coating bonded by nano-silver paste were designed for shear testing. Shear strength testing was conducted to study the influence of SiC particles proportions on the mechanical property of sintered nano-silver joints. The reliability of the bimodal nano-silver paste was evaluated experimentally by means of shear test for samples subjected to thermal aging test at 150°C and humidity and temperature testing at 85°C and 85 per cent RH, respectively. Findings Shear strength was enhanced obviously with the increase of sintering temperature and sintering time. The maximum shear strength was achieved for nano-silver paste sintered at 260°C for 10 min. There was a negative correlation between the proportion of SiC particles and shear strength. After thermal aging testing and humidity and temperature testing for 240 h, the shear strength dec...