Influence of Polycarbonate on the Crystallization Behavior of Poly(Trimethylene Terephthalate)/Polycarbonate Blends

作者：Meiling Xue, Xiangzhou Lu, Xinyu Yu, Zi-An Chen, Jiangong Wang, Zhen Li · 发表于：Journal of Macromolecular Science Part B · 年份：2019 · DOI：10.1080/00222348.2019.1587900 · 被引用次数：5 · 研究领域：Polymer crystallization and properties、biodegradable polymer synthesis and properties、Natural Fiber Reinforced Composites

To determine the factors influencing the retardation of the crystallization of poly(trimethylene terephthalate) (PTT) when PTT is blended with polycarbonate (PC), different PTT/PC blends were prepared via the melt mixing method. The relationships between the crystallization behavior and blend composition, as well as the phase morphology, were investigated. The results showed that the predominant reason for the retardation in crystallization is due to the PC content and phase morphology. The PC influences the crystallization of PTT via two methods. First, it retards PTT crystallization. Secondly, the PC exhibits a nucleation effect on the PTT crystallization which is, however, much weaker compared to the negative effect PC exerts with regards to PTT crystallization. When the processing temperature and shear rate remains unchanged, the two effects of PC determine the crystallization behavior of the blend. The phase morphology, which is strongly dependent on the mixing temperature and the shear rate, and which is also related to mixing time, had an appreciable impact on PTT crystallization. In the case of similar adhesion with the interface, a finer PC phase domain would show a slightly stronger nucleation effect on PTT crystallization.