Oxygen-vacancy-related dielectric relaxation behaviours and impedance spectroscopy of Bi(Mg1/2Ti1/2)O3 modified BaTiO3 ferroelectric ceramics

作者：Ming‐Ding Li, Xin‐Gui Tang, Si‐Ming Zeng, Yanping Jiang, Qiu‐Xiang Liu, Tianfu Zhang, Wen‐Hua Li · 发表于：Journal of Materiomics · 年份：2018 · DOI：10.1016/j.jmat.2018.03.001 · 被引用次数：105 · 研究领域：Ferroelectric and Piezoelectric Materials、Dielectric properties of ceramics、Microwave Dielectric Ceramics Synthesis

Lead-free ferroelectric ceramics (1-x) BaTiO3–xBi(Mg1/2Ti1/2)O3 (x = 0.0–0.07) were synthesized by conventional solid state reaction method and the correlation of structure, dielectric, ferroelectric and impedance properties were investigated. It was found that Tm and εm showed decreasing trend with the increase of BMT content. The high-temperature dielectric relaxation behaviour was observed in all the samples. The activation energy calculated from impedance (Ea) and conductivity (Econd), which revealed that the relaxation behaviours were linked with the migration of OVs. The values of Ea were almost equivalent to Econd. It was concluded that the short-range hopping of oxygen vacancy contributed to the dielectric relaxation and long-distance movement of doubly ionized oxygen vacancies contributed to the conduction. On the other hand, with increasing BMT contents, it was found that P-E loops became slimmer and slimmer, which indicated the increase of relaxor behaviour. The temperature dependence of P-E loops for 0.98BT–0.02BMT ceramic clearly showed the transition process from ferroelectric to relaxed ferroelectrics.