Tuning Electronic Structure of NiFe Layered Double Hydroxides with Vanadium Doping toward High Efficient Electrocatalytic Water Oxidation

作者：Pengsong Li, Xinxuan Duan, Yun Kuang, Yaping Li, Guoxin Zhang, Wen Liu, Xiaoming Sun · 发表于：Advanced Energy Materials · 年份：2018 · DOI：10.1002/aenm.201703341 · 被引用次数：761 · 研究领域：Electrocatalysts for Energy Conversion、Advanced battery technologies research、Supercapacitor Materials and Fabrication

Abstract Binary NiFe layer double hydroxide (LDH) serves as a benchmark non‐noble metal electrocatalyst for the oxygen evolution reaction, however, it still needs a relatively high overpotential to achieve the threshold current density. Herein the catalyst's electronic structure is tuned by doping vanadium ions into the NiFe LDHs laminate forming ternary NiFeV LDHs to reduce the onset potential, achieving unprecedentedly efficient electrocatalysis for water oxidation. Only 1.42 V (vs reversible hydrogen electrode (RHE), ≈195 mV overpotential) is required to achieve catalytic current density of 20 mA cm −2 with a small Tafel slope of 42 mV dec −1 in 1 m KOH solution, which manifests the best of NiFe‐based catalysts reported till now. Electrochemical analysis and density functional theory +U simulation indicate that the high catalytic activity of NiFeV LDHs mainly attributes to the vanadium doping which can modify the electronic structure and narrow the bandgap thereby bring enhanced conductivity, facile electron transfer, and abundant active sites.