Structures, Phase Transition, and Crystal Water of Fe2–xYxMo3O12

作者：Z. Y. Li, Wenbo Song, Erjun Liang · 发表于：The Journal of Physical Chemistry C · 年份：2011 · 被引用次数：78 · 研究领域：Thermal Expansion and Ionic Conductivity、Thermal and Kinetic Analysis、Microwave Dielectric Ceramics Synthesis

Materials with the formula Fe 2– x Y x Mo 3 O 12 ( x = 0.2, 0.4, 0.5, 0.6, 0.8, 1.0, 1.2, 1.4, 1.6, and 1.8) have been synthesized, and their structures, phase transitions, hygroscopicity, and thermal expansion properties have been studied by Raman spectroscopy, X-ray diffraction, and differential scanning calorimetry. It is found that Fe 2– x Y x Mo 3 O 12 crystallize in a single monoclinic for x ≤ 0.4 and a single orthorhombic structure for x ≥ 0.5. The monoclinic-to-orthorhombic phase transition temperature can be effectively decreased by increasing the contents of Y 3+ so that Fe 1.5 Y 0.5 Mo 3 O 12 crystallizes already in orthorhombic at room temperature and keeps this structure till very low temperatures (lower than 103 K). Two kinds of water species are found to present in Fe 2– x Y x Mo 3 O 12, one having little influence on the motions of the polyhedra, whereas another interacting strongly with the polyhedra and even causing a cell volume to contract. The amount of crystal water decreases with reducing the content of Y 3+ so that the motions of the polyhedra in Fe 2– x Y x Mo 3 O 12 for 0.5 ≤ x ≤ 0.8 are not obviously influenced by the crystal water. It is shown that the orthorhombic Fe 2– x Y x Mo 3 O 12 exhibit negative ( x > 1.0), near zero ( x = 1.0), and low ( x < 1.0) thermal expansion properties after the removal of the crystal water.