Effects of Dentin Surface Treatments on the Fracture Toughness and Tensile Bond Strength of a Dentin-Composite Adhesive Interface

作者：Laura E. Tam, Robert M. Pilliar · 发表于：Journal of Dental Research · 年份：1994 · DOI：10.1177/00220345940730090801 · 被引用次数：46 · 研究领域：Dental materials and restorations、Dental Implant Techniques and Outcomes、Dental Trauma and Treatments

It has been proposed that the fracture toughness test provides an appropriate method for assessing the fracture resistance of the dentin-composite interface. The plane-strain fracture toughness test was therefore applied to a dentin-composite interface, with use of a specific dentinal adhesive, so that the effects of various dentin surface treatments on dentin-bond integrity could be studied. Interfacial fracture toughness (KIC) values were determined following 24h and 180 days of specimen aging in distilled water at 37 degrees C. Tensile bond strength (TBS) results following 24-hour aging were also obtained for comparison with the 24-hour KIC results. In general, the fracture resistance of the dentin-composite interface was highest when the dentin surface was conditioned with acid but not air-dried, intermediate when the dentin surface was conditioned with acid and subsequently air-dried, and lowest when the dentin was not conditioned with acid. The tensile bond strength results differed from the fracture toughness results in indicating differences in surface preparation effects and the type of interfacial failure observed.