Synthesis of Cubic Phase Li7La3Zr2O12 Electrolyte for Solid-State Lithium-Ion Batteries

作者：Jiajia Tan, Ashutosh Tiwari · 发表于：Electrochemical and Solid-State Letters · 年份：2011 · DOI：10.1149/2.003203esl · 被引用次数：59 · 研究领域：Advancements in Battery Materials、Advanced Battery Materials and Technologies、Advanced Battery Technologies Research

We report the synthesis of high-quality cubic-phase Li 7 La 3 Zr 2 O 12 powders using a solution based technique. Detailed structural, morphological, compositional and electrochemical characterization of the samples was performed. The lithium-ion conductivity of the cubic-phase Li 7 La 3 Zr 2 O 12 , determined by electrochemical impedance spectroscopy, was ∼1.67 × 10 −4 S/cm. A proto-type all-solid-state battery with Li 7 La 3 Zr 2 O 12 as electrolyte, LiCoO 2 as cathode and a Lithium metal foil as anode was assembled. The cell was rechargeable and exhibited a very promising specific discharge capacity of 3.4 mAh/g which corresponds to 2.5% of the theoretical capacity. The above value is the highest discharge capacity reported till date using Li 7 La 3 Zr 2 O 12 electrolyte.