Effect of Micropore Topology on the Structure and Properties of Zeolite Polymer Replicas

作者：Stacy A. Johnson, Elaine S. Brigham, Patricia J. Ollivier, Thomas E. Mallouk · 发表于：Chemistry of Materials · 年份：1997 · DOI：10.1021/cm9703278 · 被引用次数：218 · 研究领域：Covalent Organic Framework Applications、Conducting polymers and applications、Concrete and Cement Materials Research

Zeolites were used as templates to prepare microporous polymer replicas. Phenol−formaldehyde polymers were synthesized and cured within the channel networks of zeolites Y, β, and L. Dissolution of the aluminosilicate framework in aqueous HF yields an organic replica that contains <2% aluminosilicate. The zeolite template exerts important topological effects on the structure and physical properties of the replica. Using zeolites Y and β, which have three-dimensionally interconnected channel structures, the microporosity of the template is reflected in the replica polymer. Pore size distributions are consistent with the predominance of 5−6 Å walls in the parent zeolite. In contrast, complete collapse of the replica, to a give nonporous material, occurs upon removal of the zeolite L template, since the latter has a one-dimensional channel structure. TEM and SEM micrographs also show evidence of collapse in the latter case. Pyrolysis of the zeolite−resin composites at 900 °C, and subsequent etching, produces very high surface area, electronically conducting replicas. Under these conditions the zeolite Y replica has markedly lower conductivity than those obtained from β and L, which have straight channels.