DURABILITY OF ENAMEL BOND STRENGTH OF SIMPLIFIED BONDING SYSTEMS

作者：Masashi Miyazaki, Masugi SATO, Hideo ONOSE · 发表于：Journal of Esthetic and Restorative Dentistry · 年份：2004 · DOI：10.1111/j.1708-8240.2004.tb00459.x · 被引用次数：32 · 研究领域：Dental materials and restorations、Dental Research and COVID-19、Dental Erosion and Treatment

ABSTRACT Objective: The purpose of this study was to determine the effect of thermal cycling on the enamel bond strengths of two‐step adhesive systems, either self‐etching primers or “one‐bottle” total‐etch systems, to bovine enamel. Materials and Methods: Three self‐etching primer systems–Imperva Fluoro Bond® (Shofu Inc., Kyoto, Japan), Clearfil® Liner Bond II (Kuraray Co. Ltd., Osaka, Japan), and Mac Bond® II (Tokuyama Corp., Tokyo, Japan)–and four total‐etch adhesive systems–One‐Step® (Bisco Inc., Schaumburg, IL, USA), Opti‐Bond Solo® (Kerr Corporation, Orange, CA, USA), Prime & Bond® 2.0 (Dentsply DeTrey, Konstanz, Germany), and Single BondTM (3M ESPE, St. Paul, MN, USA)–were used. Labial enamel surfaces of bovine incisors were exposed by grinding with 240‐grit and 600‐grit wet silicon carbide paper. Enamel was treated according to the manufacturers' instructions. Following the application of adhesive resin, resin composites were condensed into a mold (diameter = 4 mm, depth = 2 mm) and were light‐cured. Bonded specimens were stored in 37°C water for 24 hours. They were divided into a control group (no thermal cycling) and three experimental groups with thermal cycles of 3,000, 10,000, and 30,000 cycles, respectively, between 5°C and 60°C. The shear test was performed at a crosshead speed of 1.0 mm/min. The ultrastructure of resin‐enamel interfaces was observed by SEM at times 3,500 magnification. Results: Self‐etching primer systems had significant decreases in enamel bo...