Antisite defect elimination through Mg doping in stoichiometric lithium tantalate powder synthesized via a wet-chemical spray-drying method

作者：Dehui Sun, Xueliang Kang, Qian Yu, Kun Cui, Xiaoyong Qin, Xuxia Shi, Huaqiang Cai, T. Ohachi, Yuanhua Sang, Hong Liu · 发表于：Journal of Applied Crystallography · 年份：2015 · DOI：10.1107/s1600576715002113 · 被引用次数：7 · 研究领域：Ferroelectric and Piezoelectric Materials、Microwave Dielectric Ceramics Synthesis、Photorefractive and Nonlinear Optics

MgO-doped stoichiometric LiTaO 3 (MgO:SLT) is one of the most promising nonlinear materials. However, its industrial application is limited by the poor optical quality caused by the nonhomogeneous distribution of magnesium. Herein, an MgO:SLT polycrystalline powder was synthesized with a homogenous magnesium distribution by a wet-chemical spray-drying method. A comparative investigation of the coordination state of Ta ions in MgO:SLT powders synthesized by this method and by a conventional solid-state reaction method was performed by X-ray photoelectron spectroscopy. It is proved that the Ta–Li antisite was completely eliminated as a result of the homogeneous Mg doping in the SLT lattice using the wet-chemical spray-drying method. However, for MgO:LT powder produced by the solid-state reaction method, element analysis after acid treatment shows that some Mg ions did not enter the LT lattice after high-temperature calcination. Also, scanning electron microscopy and transmission electron microscopy energy dispersive spectroscopy verified that some MgO particles still exist in the as-synthesized MgO:LT powder. This synthesis method can be used for mass production of high-quality polycrystalline powders for doped crystal growth and some other doped oxide powder products with high melt point.