OPTIMIZATION OF DISSOLUTION OF ULEXITE IN (NH4)2SO4SOLUTIONS

作者：Özkan Küçük, M. Muhtar Kocakerìm, Mehmet Çopur, Ahmet Yartaşı · 发表于：Canadian Metallurgical Quarterly · 年份：2005 · DOI：10.1179/cmq.2005.44.1.53 · 被引用次数：10 · 研究领域：Crystallization and Solubility Studies、Mineral Processing and Grinding、Minerals Flotation and Separation Techniques

The Taguchi method was used to determine the optimum conditions for the dissolution of ulexite in ammonium sulphate solutions. The ranges of experimental parameters were between 60-88 °C for reaction temperature, 0.05-0.15 g.mL−1 for solid to liquid ratio, 5–20 minutes. for reaction time and (-850+600) – (−90) μm for particle size. The optimum conditions for these parameters were found to be 88 °C, 0.1 g.mL−1, −90 μm and 20 minutes, respectively. Under these conditions, the predicted and experimental dissolution percentages of ulexite in ammonium sulphate solutions were 98.60 and 98.36 per cent, respectively.On a utilisé la méthode de Taguchi pour déterminer les conditions optimales de dissolution de l’ulexite dans des solutions de sulfate d’ammonium. La gamme des paramètres expérimentaux se situait entre 60-88°C pour la température de réaction, entre 0.05−0.15 g·mL−1 pour le rapport solide–liquide, entre 5−20 min pour la durée de réaction et entre (−850+600) – (−90) μm pour la taille de particule. On a trouvé que les conditions optimales des paramètre étaient de 88°C, 0.1 g·mL−1, −90μm et 20 min, respectivement. Sous ces conditions, le pourcentages prédit et le pourcentage expérimental de dissolution de l’ulexite dans des solutions de sulfate d’ammonium étaient de 98.60 et de 98.36 pourcent, respectivement.