The mechanical design of nacre

作者：Andrew Jackson, Julian F. V. Vincent, R. M. Turner · 发表于：Proceedings of the Royal Society B Biological Sciences · 年份：1988 · DOI：10.1098/rspb.1988.0056 · 被引用次数：1273 · 研究领域：Calcium Carbonate Crystallization and Inhibition、Paleontology and Stratigraphy of Fossils、Bone Tissue Engineering Materials

Abstract Mother-of-pearl (nacre) is a platelet-reinforced composite, highly filled with calcium carbonate (aragonite). The Young modulus, determined from beams of a span-to-depth ratio of no less than 15 (a necessary precaution), is of the order of 70 GPa (dry) and 60 GPa (wet), much higher than previously recorded values. These values can be derived from ‘shear-lag’ models developed for platey composites, suggesting that nacre is a near-ideal material. The tensile strength of nacre is of the order of 170 MPa (dry) and 140 MPa (wet), values which are best modelled assuming that pull-out of the platelets is the main mode of failure. In three-point bending, depending on the span-to-depth ratio and degree of hydration, the work to fracture across the platelets varies from 350 to 1240 J m-2. In general, the effect of water is to increase the ductility of nacre and increase the toughness almost tenfold by the associated introduction of plastic work. The pull-out model is sufficient to account for the toughness of dry nacre, but accounts for only a third of the toughness of wet nacre. The additional contribution probably comes from debonding within the thin layer of matrix material. Electron microscopy reveals that the ductility of wet nacre is caused by cohesive fracture along platelet lamellae at right angles to the main crack. The matrix appears to be well bonded to the lamellae, enabling the matrix to be stretched across the delamination cracks without breaking, thereby sustain...